Pooling Polyurethane Coating

• Customization: Available
• Certification: ISO, CE
• Material: Polyurethane, PU
• Model NO.: coating
• Type: Roofing and Waterproofing
• Function: Waterproof
• Color: White
• Usage: Outdoor, Indoor
• After-sales Service: One Year
• Warranty: One Year
• Ceiling Tile Shape: /
• Thickness: /
• Ceiling Tile Type: /
• Surface Treatment: /
• Transport Package: Barrel
• Specification: 20kg/barrel
• Trademark: fengyuan
• Origin: China
• HS Code: 3918109000
• Production Capacity: 1000000

Product Description

Single-component Polyurethane Waterproof Coating
Product Overview

Single-component Polyurethane Waterproof Coating is reaction-type ,moisture, and film-forming macromolecular coating .With isocyanate and polyether polyalcohol as the main material, and mixed with several assistants and filling material ,the product is made through addition polymerization reaction. In construction ,the coating is directly painted on waterproof based layer.

Advantages
Single package and open -to-use for convenient construction ;
Pure polyurethane film for high tensile strength, better elongation, and excellent temperature performance to withstand temperature and stress shrinkage and expansion of based layer;
High elasticity and extensibility of film forming ,no crack.
Weather resistance ,acid & alkali resistance and strong adhesive properties .
Environment mental protecting product.

Application Scope roofing ,basement ,bathroom ,
swimming pool, and a variety of civil and industrial buildings. It is also applicable to waterproofing of places with complicated shapes and crisscrossed pipes.

Executive standard (GB/T19250 -2013)

Item		Index
		Type 1	Type2
Solid content (%) ≥		85
Dry Time (h)	Surface ≤	12
	Body  ≤	24
Tensile Strength (Mpa ) ≥		2.0	6.0
Breaking Elongation (%)≥		500	450
Impermeability (0.3Mpa,30min )		Impermeable
Low-temperature Flexural Endurance		-35ºC.no fissure
Adhesive strength (Mpa )  ≥		1.0

Double -component chemical reaction curing waterproof coating
 
Product Overview
Double-component chemical reaction curing waterproof coating ,with isocyanate-blocked pre-polymer (poly-condensed with polyether and isocyanate )as Component A and colored liquid (comprised of plasticizer ,curing agent ,thickening agent ,coagulant ,and filler)as Components are mixed in certain proportion ,and evenly painted on the surface of waterproof based .so as to form rubber elastic film upon cross-linking and solidification under normal temperature.

Advantages

Form dense film ,no bubble or pore .
Strong adhesive strength with concrete ,wood ,metal, and ceramic material ;
Flame-free construction :simply by mixing the two component
No coaltar or other harmful subatstance;


Application Scope

The product may be applied in waterproof works for non-exposed roofing ,underground structure ,bath room ,kitchen ,balcony, waterproof pool, parking area, etc. It is also applicable to waterproof treatment for position with complicates and pipes.
 

Item		Index
		Type 1	Type 2	Type 3
Solid Content (%) ≥		92.0
Dry time (h)	Surface dry ≤	12
	Body dry ≤	24
Tensile strength ≥		2.00	6.00	12.00
Breaking Elongation (%)≥		500	450	250
Impermeability (0.3Mpa,30min )		Impermeable at 0.3Mpa for 120min
Low-temperature Flexural Endurance		-35ºC,no fissure
Adhesive strength (Mpa )  ≥		1.0